From: Probing the transition from dislocation jamming to pinning by machine learning
ρp [m−3]
σc[·107 Pa]
1.0·1018
1.10
2.0·1018
1.25
5.1·1018
1.40
1.0·1019
1.70
2.0·1019
2.25
5.1·1019
3.50
1.0·1020
4.50
2.0·1020
6.25
4.1·1020
9.00
1.0·1021
14.0