From: Probing the transition from dislocation jamming to pinning by machine learning
Parameter | Value |
---|---|
System size L | 4 μm |
Initial dislocation density ρ0 | 2.0×1012 m−2 |
b | 0.286 nm |
rcore | 5.0 b |
Maximum segment length | 80.0 b |
G | 26 GPa |
ν | 0.35 |
T | 300 K |
ParaDiS mobility function | FCC_0b |
Medge | 10000.0 (Pa s)−1 |
Mscrew | 10000.0 (Pa s)−1 |
A | 2.3·10−19 Pa m3 |
rp | 28.6 nm |