Fig. 1From: Diffuse-interface polycrystal plasticity: expressing grain boundaries as geometrically necessary dislocationsIn two-dimensions, the above construction results in exactly two non-zero components (G 31 and G 32) of G. In particular, for a symmetric tilt boundary oriented as shown above, G 32≡0 when θ is a step functionBack to article page